Evaluation of the Interest of NiMo Catalysts Supported on MgO?TiO2 for Hydrodesulfurization Applications



Guevara Lara, Alfredo

2019

López-Benítez, A., Berhault, G., Silva-Rodrigo, R., Rodríguez-Ávila, J.A., Vrinat, M., Guevara-Lara, A. Evaluation of the Interest of NiMo Catalysts Supported on MgO?TiO2 for Hydrodesulfurization Applications. Catal Lett (2019) 149: 2656. https://doi.org/10.1007/s10562-019-02831-6


Abstract


A series of NiMo catalysts supported on MgO?TiO2 (5 mol% TiO2) were prepared and evaluated in hydrodesulfurization applications. The MgO?TiO2 support was obtained by the sol?gel method. The as-obtained MgO?TiO2 support was then impregnated with nickel nitrate, Ni(NO3)2.6H2O and ammonium heptamolybdate, (NH4)6Mo7O24.4H2O aqueous solutions at pH 9 and pH 5. Subsequently, catalysts were characterized at each step of the preparation: after drying and calcination steps using UV?vis diffuse reflectance (UV?vis-DRS) and Raman spectroscopies and after sulfidation by X-ray photoelectron spectroscopy and transmission electron microscopy. The resulting NiMo catalysts were evaluated in hydrodesulfurization, using thiophene (TP) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) as representative sulfur-containing screening molecules. Finally, catalysts were evaluated in a light cycle oil (LCO) hydrodesulfurization reaction. The pH of the impregnation solution of Ni and Mo precursors influences only slightly the nature of the Ni and Mo species formed. Moreover, in both cases, a significant proportion of nickel is lost into spinel compounds leading to a lower propensity of Ni to be accommodated on the edges of MoS2 slabs decreasing the ability to sulfide correctly the NiMo catalysts. Therefore, MgO appears as a too strong interacting support consuming nickel and forming HDS inactive phases even if the addition of TiO2 tends to enhance textural properties.



Producto de Investigación




Artículos relacionados

Evaluación de Esteroides Aromáticos como Indicadores de Madurez Térmica en Extractos de Roca

A theoretical quantum study on the distribution of electrophilic and nucleophilic active sites on th...

Analysis of the experimental pressuretemperature behavior in the isotropicnematic phase transition f...

Efecto de la composición del soporte sobre las estructuras superficiales de óxidos de níquel y molib...

A Semiempirical PM6 Study of Some Aminopyrimidine Derivatives and their Interaction with an Iron Sur...

THEORETICAL STUDY ON THE MODIFICATION OF ACTIVE SITES IN GOLD SURFACES MODELED AS FINITE CLUSTERS: I...

Morphological and magnetic properties of cobalt nanoclusters electrodeposited onto HOPG

The role of temperature in copper electrocrystallization in ammoniachloride solutions

Nucleation and Growth Kinetics of Electrodeposited Sulfate-Doped Polypyrrole: Determination of the D...

Synthesis and crystal structures of cis-palladium(II) and cis-platinum(II) complexes containing di...